Italfil ER110S-G IT-T1s High Tensile Solid Wire 1.2mm 15kg

MADE IN ITALY All Positional Solid MIG/MAG Copper coated low alloy steel Welding Wire for High Strength Steels ER110S-G is a 0.3Cr-1.5Ni-0.3Mo-alloyed, copper coated solid wire, for MIG/MAG of high strength steels with low-temperature impact toughness requirements. Characteristic features include excellent start properties, trouble-free feeding at high wire speeds and lengthy feed distances, a very stable arc at high welding currents; extremely low levels of spatter, low fume emission.` Capable of producing welds with 690 MPa (100 ksi) tensile strength. Excellent for welding quenched and tempered steels and HY-80 base materials. Supports short-circuiting, globular, axial spray and pulsed spray transfer. Classification: AS/NZS: 16834-B-G 78 A 5U M21 G A5.28/ASME SFA5.28 ER110S-G EN ISO: 16834-A-G 69 4 M21 Mn3Ni1CrMo All Positions Interpass 120-180 Deg Operating amps 1.2mm 220-320A Operating volts 1.2mm 22-28mm Copper coated low-alloy wire with Ni-CrMo suitable for single pass or multipass welding of low-alloy steels. It can be used also when good toughness characteristics in low temperature are requide. Applications: Structural steel Transport industry Heavy equipment Earth moving Crane repairs and fabrication Weldox 700 Low alloy Steel and suitable for welding high Tensile steels such as T1, Bisalloy 80, AISI 4140. Shielding Gas: Argon + CO2(M20,M21,M33) Current and Polarity DC+ Base Material to be welded T1, T1A, T1B, HY90, N-A-XTRA 56-63-65-70, X65, X70, X80, S460, S500, S550, S620, S690, WELDOX 700, BISALLOY 80, WELTEN 80 etc. Typical Welding Chemistry: C/0.089 Si/0.60 Mn/1.60 P/0.015 S/0.015 Cu/0.25 Cr/0.30 Ni/1.50 Mo/0.30 Al/0,030 V/0.10 Ti/0.050 Zr/0.050 Typical mechanical properties of weld metal: Tensile Strength 800 MPa Yield Strength 750 MPa Elongation 19.4% Temp/-40C Elongation 19.4% Temp/-40C AS/NZS: 16834-B-G 78A 5U M21 G (OLD AS/NZS: 2717.1:1996 ESMG-GM-W769AH)